Structural investigation of iron sulfides

Structural investigation of iron sulfides
上海漾盟仪器有限公司更新于：2011-11-03

应用行业：纺织/印染/服装/皮革纺织原料

立即扫码咨询

联系方式：400-822-6768

联系我们时请说明在仪器网（www.yiqi.com）上看到的!

Abstract In the current study, pure elemental powders of Fe and S were mixed to give the desired compositions of Fe67S33, Fe50S50 and Fe33S67. A SPEX 8000D high-energy ball mill was used to synthesize iron sulfide powders under an Ar-filled atmosphere. The as-milled powders were examined by conventional X-ray diffraction (XRD) and synchrotron X-ray absorption spectroscopy (XAS). The experimental results showed that mechanochemical reactions occurred during the ball mil领 process for all the compositions investigated. The Fe1−xS phase was observed at the end of mil领. The formation time of the Fe1−xS phase increased with increasing sulfur content. Extended X-ray absorption fine structure (EXAFS) results revealed that the nearest neior bond lengths of the radial distribution function for iron decreased when iron sulfides formed. X-ray absorption near-edge structure (XANES) of sulfar K-edges distinguished better the structural evolution of these iron sulfides. © 2003 Elsevier B.V. All rights reserved. SPEX8000D 高能量球磨机

仪器网（yiqi.com）欢迎您！